PolyLite™ PLA Pro
Last updated
Was this helpful?
Last updated
Was this helpful?
Polylite™ PLA Pro is a first of its kind combining high toughness and high rigidity, this professional PLA offers engineering properties with the ease of print of regular PLA.
PHYSICAL PROPERTIES
Density
ISO1183,GB/T1033
1.22 g/cm3 at 21.5℃
Melt index
210℃,2.16kg
6g/10min
Light transmission
N/A
N/A
Flame retardancy
N/A
N/A
CHEMICAL RESISTANCE DATA
Effect of weak acids
Not resistant
Effect of strong acids
Not resistant
Effect of weak alkalis
Not resistant
Effect of strong alkalis
Not resistant
Effect of organic solvent
No data available
Effect of oils and grease
No data available
Glass transition temperature
DSC, 10°C/min
62 °C
Melting temperature
DSC, 10°C/min
150 °C
Crystallization temperature
DSC, 10°C/min
N/A
Decomposition temperature
TGA, 20°C/min
N/A
Vicat softening temperature
ISO 306, GB/T 1633
62.7 °C
Heat deflection temperature
ISO 75 1.8MPa
57.6 °C
Heat deflection temperature
ISO 75 0.45MPa
59.3 °C
Thermal conductivity
N/A
N/A
Heat shrinkage rate
N/A
N/A
Young’s modulus (X-Y)
ISO 527, GB/T 1040
2932.2 ± 55.3 MPa
Young’s modulus (Z)
ISO 527, GB/T 1040
2633.0 ± 117.4 MPa
Tensile strength (X-Y)
ISO 527, GB/T 1040
49.8 ± 0.4 MPa
Tensile strength (Z)
ISO 527, GB/T 1040
36.5 ±0.6 MPa
Elongation at break (X-Y)
ISO 527, GB/T 1040
6.3 ± 0.9 %
Elongation at break (Z)
ISO 527, GB/T 1040
2.4 ± 0.3 %
Bending modulus (X-Y)
ISO 178, GB/T 9341
2933.8 ± 78.3 MPa
Bending modulus (Z)
ISO 178, GB/T 9341
N/A
Bending strength (X-Y)
ISO 178, GB/T 9341
77.9 ± 0.4 MPa
Bending strength (Z)
ISO 178, GB/T 9341
N/A
Charpy impact strength (X-Y)
ISO 179, GB/T 1043
17.1 ±1.2 kJ/m2
Charpy impact strength (Z)
ISO 179, GB/T 1043
N/A
Based on 0.4 mm nozzle and Simplify 3D v.4.0. Printing conditions may vary with different nozzle diameters
Nozzle temperature
190 – 220 (℃)
Build surface material
BuildTak®, Glass, Blue Tape
Build surface treatment
Glue or Magigoo
Build plate temperature
30 - 60 (˚C)
Cooling fan
ON
Printing speed
30-70 (mm/s)
Raft separation distance
0.2 (mm)
Retraction distance
1 - 3 (mm)
Retraction speed
30 - 60 (mm/s)
Environmental temperature
0 - 40 (˚C)
Threshold overhang angle
60 (˚)
Recommended support material
PolySupport™ and PolyDissolve™ S1
ISO 527, GB/T 1040
ISO 179,GB/T 1043
*All specimens were conditioned at room temperature for 24h prior to testing
Bed temperature
25 °C
Shell
2
Top & bottom layer
4
Infill
100 %
Environmental temperature
25 ˚C
Cooling fan
ON
The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End- use performance of printed parts depends not only on materials, but also on part design,environmental conditions, printing conditions, etc. Product specifications are subject to change without notice.
Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/ recycling practices of Polymaker materials for the intended application. Polymaker makes no warranty of any kind, unless announced separately, to the fitness for any use or application. Polymaker shall not be made liable for any damage,injury or loss induced from the use of Polymaker materials in any application.