Fiberon™ PA6-CF20

Fiberon™ PA6-CF20 is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion.

Fiberon™ PA6-CF20 is the same great formula as PolyMide PA6-CF, although Fiberon™ PA6-CF20 may print in a slightly darker black shade color than its predecessor.

Printing Recommendations

Nozzle temperature	280 - 300°C
Build plate temperature	40 - 50°C
Environmental temperature	Room Temperature
Fan speed	0%
Printing speed	30 - 300 mm/s

Printing Tips

his material has a requirement that you print with an all metal hotend that can reach 280˚C or higher as well as the need for a hardened nozzle.

• Do not set your build plate above 50˚C and keep any chamber doors open. If you let the build plate or ambient air get above 50˚C, you run the risk of warping or ugly prints.

• Use a glue stick or Magigoo PA if experiencing any issues with bed adhesion.

• PA-CF is very hygroscopic and therefore should only be printed while kept in a heated filament dryer the entire time you print.

• If you hear "popping" or "cracking" noises, then the filament needs to be dried.

• This needs to be annealed after printing at 100˚C for 16 hours.

• After annealing - the part will be dried out and therefore need to be moisture conditioned.

• Moisture conditioning will happen even if you do nothing as the material absorbs moisture from the air. To speed up moisture conditioning, keep in a humid environment for 48 hours.

FAQ

What is annealing?

You can find out more about annealing HERE.

What is moisture conditioning?

Moisture conditioning refers to allowing the print to absorb moisture. This is inevitble since nylons are hygroscopic, but you can expedite the process by keeping the print in a high humidity climate, or submerging them in water, for 48 hours. All of our test specimens were annealed at 100˚C for 16 hours, and then immerged in water at 60˚C for 48 hours. The average moisture content of specimens is 2.57%.

Read more about moisture conditioning HERE.

Should I anneal before or after moisture conditioning?

IWhen you anneal in a convection oven, you will dry the part out. So if you moisture condition before annealing - you will need to moisture condition again after. So we would suggest to moisture condition after annealing.

Why do you use such a low build plate temperature with your nylons?

Our nylons come with our Warp-Free™ Technology. In order for this Warp-Free™ technology to work as it should - we want to make sure the build plate and the ambient air temperatures are both below 50˚C. We then anneal the print after to get it's full strength.

Learn more HERE

Will the spools work in an AMS?

Yes! We have redesigned the edges of our spools so all Polymaker products will now spin great in the AMS.

That said - you will need to be careful when using any abrasive materials in the AMS.

Do I need a filament dryer?

Yes, you will need a filament dryer when printing with nylons due to them being hygroscopic.

Printing Requirements

• All-metal hotend 280˚C+

• Hardened nozzle

• Filament dryer

• Annealing post printing

• Moisture conditioning after Annealing